Product Description:
It can balance high impact resistance/rigidity and glossiness,
Universal molded materials for electroplating, decorative accessories, audio equipment panels, wheel covers, toiletries, and clock casings.
Product Description:
It can balance high impact resistance/rigidity and glossiness,
Universal molded materials for electroplating, decorative accessories, audio equipment panels, wheel covers, toiletries, and clock casings.
Material Technical Data Sheet | ||||
ABS -10 PA-727 Plating grade ABS | ||||
characteristic | Application Area | |||
Electroplating specific | decorative accessories | |||
High impact resistance | Audio equipment panel components | |||
High gloss | auto parts | |||
high rigidity | toiletries | |||
Physical Property | ||||
characteristic | Testing standards | Test conditions | Unit | Typical value |
proportion | ISO 1183 | 23℃ | g/cm³ | 1.05 |
Mold Shrinkage | ISO 294-4 | % | 0.4~0.7 | |
Melt Index | ISO 1133 | 220℃ X10KG | ml/10 min | 19 |
Mechanical Property | ||||
Mechanical Property | Testing standards | Test conditions | Unit | Data |
tensile strength | ISO 527 | 50mm/min | mpa | 46 |
Elongation rate | ISO 527 | 50mm/min | % | 50 |
bending strength | ISO 178 | 2mm/min | MPA | 71 |
Bending elastic modulus | ISO 178 | 2mm/min | GPA | 2 |
IZOG impact strength with a gap | ISO 180/1A | 23℃ | KJ/㎡ | 24 |
IZOG impact strength with a gap | ISO 180/1A | -30 | KJ/㎡ | 11 |
Thermal Property | ||||
Thermal Property | Testing standards | Test conditions | Unit | Data |
Non-burning-out Heat distortion temperature | ISO 75/A | 1.8MPa | ℃ | 83 |
burning-out Heat distortion temperature | ISO 75/A | 1.8MPa | ℃ | 100 |
Injection molding | ||||
Injection molding | Unit | Data | ||
drying temperature | ℃ | 80~85 | ||
drying time | H | 3~4 | ||
Front measuring area Temperature | ℃ | 230~190 | ||
Mid compression zone Temperature | ℃ | 230~190 | ||
Third section feeding zone Temperature | ℃ | 220~180 | ||
Maximum melting temperature | ℃ | 240 | ||
mold temperature | ℃ | 30~70 | ||
injection speed | Medium low speed |
Thermal Properties | ||||
Thermal Properties | Test Standard | Test Condition | Units | Data |
UL | ASTMD495 | |||
Flame Retardancy | ||||
Flame Retardancy | Test Standard | Data | ||
Fire Rating Full Color 1.5mm | UL94 | HB | ||
Fire Rating Full Color 3.0mm | UL94 | HB | ||
Ul | ||||
Flame Retardancy | Test Standard | Data | Units | |
Fire Rating Full Color 1.5mm | UL94 | HB | ||
Fire Rating Full Color 3.0mm | UL94 | HB | ||
HAI Full Color 1.5mm | UL746A | 0 | PLC | |
HAI Full Color3.0mm | UL746A | 0 | PLC | |
RTI Elec Full Color 1.5mm | UL746B | 60 | ℃ | |
RTI Elec Full Color 3.0mm | UL746B | 60 | ℃ | |
RTI Imp Full color1.5MM | UL746B | 60 | ℃ | |
RTI Str Full color1.5MM | UL746B | 60 | ℃ | |
RTI Str Full color3.0MM | UL746B | 60 | ℃ |
Material Technical Data Sheet | ||||
ABS -10 PA-727 Plating grade ABS | ||||
characteristic | Application Area | |||
Electroplating specific | decorative accessories | |||
High impact resistance | Audio equipment panel components | |||
High gloss | auto parts | |||
high rigidity | toiletries | |||
Physical Property | ||||
characteristic | Testing standards | Test conditions | Unit | Typical value |
proportion | ISO 1183 | 23℃ | g/cm³ | 1.05 |
Mold Shrinkage | ISO 294-4 | % | 0.4~0.7 | |
Melt Index | ISO 1133 | 220℃ X10KG | ml/10 min | 19 |
Mechanical Property | ||||
Mechanical Property | Testing standards | Test conditions | Unit | Data |
tensile strength | ISO 527 | 50mm/min | mpa | 46 |
Elongation rate | ISO 527 | 50mm/min | % | 50 |
bending strength | ISO 178 | 2mm/min | MPA | 71 |
Bending elastic modulus | ISO 178 | 2mm/min | GPA | 2 |
IZOG impact strength with a gap | ISO 180/1A | 23℃ | KJ/㎡ | 24 |
IZOG impact strength with a gap | ISO 180/1A | -30 | KJ/㎡ | 11 |
Thermal Property | ||||
Thermal Property | Testing standards | Test conditions | Unit | Data |
Non-burning-out Heat distortion temperature | ISO 75/A | 1.8MPa | ℃ | 83 |
burning-out Heat distortion temperature | ISO 75/A | 1.8MPa | ℃ | 100 |
Injection molding | ||||
Injection molding | Unit | Data | ||
drying temperature | ℃ | 80~85 | ||
drying time | H | 3~4 | ||
Front measuring area Temperature | ℃ | 230~190 | ||
Mid compression zone Temperature | ℃ | 230~190 | ||
Third section feeding zone Temperature | ℃ | 220~180 | ||
Maximum melting temperature | ℃ | 240 | ||
mold temperature | ℃ | 30~70 | ||
injection speed | Medium low speed |
Thermal Properties | ||||
Thermal Properties | Test Standard | Test Condition | Units | Data |
UL | ASTMD495 | |||
Flame Retardancy | ||||
Flame Retardancy | Test Standard | Data | ||
Fire Rating Full Color 1.5mm | UL94 | HB | ||
Fire Rating Full Color 3.0mm | UL94 | HB | ||
Ul | ||||
Flame Retardancy | Test Standard | Data | Units | |
Fire Rating Full Color 1.5mm | UL94 | HB | ||
Fire Rating Full Color 3.0mm | UL94 | HB | ||
HAI Full Color 1.5mm | UL746A | 0 | PLC | |
HAI Full Color3.0mm | UL746A | 0 | PLC | |
RTI Elec Full Color 1.5mm | UL746B | 60 | ℃ | |
RTI Elec Full Color 3.0mm | UL746B | 60 | ℃ | |
RTI Imp Full color1.5MM | UL746B | 60 | ℃ | |
RTI Str Full color1.5MM | UL746B | 60 | ℃ | |
RTI Str Full color3.0MM | UL746B | 60 | ℃ |